Near Shore and on Shore: Materials of Construction

From MDOT Policy Manual
Revision as of 15:19, 10 January 2017 by Mnemphos (talk | contribs) (Created page with "=Primary Guidance= ==Concrete== *Marine Mix Design **Certify using independent commercial testing laboratory with testing conducted within last 6 months **Applicability: all...")
(diff) ← Older revision | Latest revision (diff) | Newer revision → (diff)
Jump to: navigation, search

Primary Guidance

Concrete

  • Marine Mix Design
    • Certify using independent commercial testing laboratory with testing conducted within last 6 months
    • Applicability: all in-water concrete including but not limited to piles, pile and sheet caps, precast deck panels, fascia beams, and outfalls. Spec link here.
  • SCC: all precast members, closure pours between precast elements
  • RCC: RCC or asphalt overlaid RCC in travel lanes and stern ramp landing pads on ro ro berths where tracked vehicles are transferred

Reinforcement

  • Corrosion resistant: investigate cost, local availability, contractor experience and utilize where feasible, especially alloys that do not corrode for in-water structural elements

Structural steel

  • Cathodic Protection (CP): passive CP system for all structural steel in contact with water with minimum 25 yr design life; passive or active system as required to mitigate stray currents from CP systems of layberthed vessels; stray current investigation for all submerged structural steel within 500 ft of layberthing terminal for vessels with CP systems

Timber

  • non-commercial, non-industrial facilities only.

==Surface course of pavement o Highway trucks: no special requirements o Superload trailers/mafis: solid tire vehicles require durable surface course and low speeds o Forklifts: concrete for axle loads > 27,000# o Outriggers: RCC prohibited in the absence of matting o Track vehicles: RCC, asphalt overlaid RCC or concrete pavers Discussion

Concrete

Waterfront facilities composed of conventional highway concrete mix designs demonstrate materials-related service levels below half the service life expectation. Adequately performing marine concretes are both highly impermeable to water-born chlorides and sulfates and immune to expansive deterioration due to the formation of ettringite, whether that formation is the result of aggregate reactivity or high temperature curing of precast concrete. Ion transfer analyses are one method of estimating the service life of a given mix while empirical data is developed.

Reinforcement
Deterioration of waterfront facilities due to corrosion of concrete reinforcement can be deferred or avoided by the selection of corrosion-resistant reinforcement. The onset of corrosion is not necessarily a late term effect but can occur at any time an incident causes cracking damage, whether due to environmental storms, accidents involving equipment or vessel berthing.
Structural Steel

Placement of carbon steel members in water should be avoided where possible. Protective coatings have a finite service life and are prone to holidays. Existing steel piles and new sheeting require a passive CP system to prevent rapid corrosion and section loss, especially where vessels are layberthed.

Timber

Timber structures are not appropriate in industrial settings due to their inherent weak material strengths and susceptibility to soft rot.

Surface Course of Pavement

Durable surface courses are required in travel lanes for tracked vehicles to resist aggressive surface stripping in turning maneuvers.